EASY TO CLEAN COATINGS:

Easy to clean Coating: AAC 2000 EC

AAC 2000 EC is an advanced 1K solvent-based coating system, completely free of fluorocarbons, designed for high-temperature curing in special industrial applications. It offers robust protection for various substrates exposed to harsh conditions, including extreme temperatures, corrosion, light, moisture, salt, and dirt. This coating provides an exceptional combination of release and easy-to-clean properties, ensuring superior durability against chemicals, mechanical stress, light, and thermal fluctuations. Ideal for challenging environments, AAC 2000 EC delivers long-lasting performance and reliable protection.

Key Features

  • PFA-free
  • Hydrophobic surface
  • Easy-to-clean
  • Non-stick and release effect
  • Dense and compact coating
  • Abrasion resistance
  • Chemical and thermal resistance
  • UV resistance, no discoloration
  • Good barrier to oxygen and water
  • Good adhesion to various substates

Physical Features

  • Appearance: transparent
  • Color: colorless
  • Solid Content: 37.1 %
  • Density (23°C): 0.92 g/cm3
  • Viscosity (23°C): 16-39 cP
  • Curing conditions:
    • At 130°C for 3h
    • At 160°C for 1h

Technical Data

  • Water contact angle: 110-116°
  • Surface Energy (WORK Method): 16-18 mN/m
  • Water roll-off angle: 16-17°
  • Cured Film Thickness: up to maximum 15 μm (recommended)
  • Adhesion (Cross Hatsch Test ASTM D3359, Method B): ASTM (ISO) Class 5B (0)
  • Abrasion Resistance: Mass Loss <1mg (CS-10 Calibrase, 500g load, 200 cycles)
  • UV Resistance (ISO 16474-3 C1): No visual damage, no hydrophobicity loss after 3000 hours
  • Oxygen/Water barrier (boiling water vapors): No visual damage, no hydrophobicity loss after 24 hours

For detailed specifications and application guidelines, please refer to the Technical Data Sheet.

For safety information (SDS), please contact us.

Easy to clean Coating: AAC 1110 EC

AAC 2110 EC is a 2K solvent-based, room temperature curing system for specialized industrial applications. It offers a perfect combination of electrical conductivity and non-stick properties as well as resistance to chemicals and thermal fluctuations. AAC 1110 EC is the optimal solution for all types of surfaces exposed to heavy contamination, where electrical conductivity is required. AAC 1110 EC delivers long-lasting performance and reliable protection.

Key Features

  • PFA-free
  • Electrically conductive coating
  • Hydrophobic surface
  • Easy-to-clean
  • Non-stick effect
  • Dense and compact coating
  • Abrasion resistance
  • Chemical and thermal resistance

Physical Features

  • Appearance: opaque
  • Color: black
  • Solid Content: 45.1 %
  • Density (23°C): 0.95 g/cm3
  • Viscosity (23°C): 37-47 cP
  • Mix Ratio (A:B): 1.7 : 3.3
  • Curing conditions:
    • Dry-to-touch at room temperature after 30 min.
    • Fully cured at room temperature after 24 hours.

Technical Data

  • Water contact angle: 107-109°
  • Surface Energy (OWRK Method): 17-19 mN/m
  • Water roll-off angle: 21-25°
  • Cured Film Thickness: up to maximum 10 μm (recommended)
  • Abrasion Resistance: Mass Loss 2.2mg (CS-10 Calibrase, 500g load, 200 cycles)

For detailed specifications and application guidelines, please refer to the Technical Data Sheet.

For safety information (SDS), please contact us.

Easy to clean Coating: AAC 3000 EC

The AAC 3000 EC is a high-performance, fluorocarbon-free 2K solvent-based hybrid transparent coating. Applied and cured at room temperature, it protects components of various sizes and shapes in harsh environments. Its durability, easy-to-clean properties, and resistance to chemicals, mechanical stress, and light make it ideal for demanding industrial applications.

Key Features

  • PFA-free
  • Easy-to-clean
  • Release and non-stick effect
  • Ultra high solids
  • Room temperature curing
  • Abrasion Resistance
  • Scratch resistance
  • UV and chemical resistant
  • Good adhesion to various substrates

Physical Features

  • Appearance: transparent
  • Color: colorless
  • Solid Content: > 90%
  • Mix Ratio 1 (A:B): 4 : 1
  • Curing conditions 1:
    • Dry-to-touch at room temperature after 10 hours.
    • Full chemical / mechanical properties (rt) after 14 days
  • Mix Ratio 2 (A:B:AC): 4 : 1.2 : 0.8
  • Curing conditions 2:
    • Dry-to-touch at room temperature after 1 hour.
    • Dry-through at room temperature after 4 hours
    • Full chemical / mechanical properties (rt) after 14 days

Technical Data

  • Water contact angle: 111-112°
  • Surface Energy (OWRK Method): 19-21 mN/m
  • Water roll-off angle: 24-25°
  • Cured Film Thickness: up to 30 μm
  • Abrasion Resistance: Mass Loss <2mg (CS-10 Calibrase, 500g load, 200 cycles)

For detailed specifications and application guidelines, please refer to the Technical Data Sheet.

For safety information (SDS), please contact us.

ANTI ICE COATINGS:

AAC 2000 AI

AAC 2000 AI is an advanced solvent-based coating tailored for anti-icing needs. This 1K formula is free of fluorocarbons and offers excellent protection in extreme conditions like cold, hot, moisture, and corrosion. It cures at high temperatures, effectively preventing ice build-up and reducing ice adhesion, making it easier to remove ice and snow, thus minimizing operational interruptions. Additionally, its superior release and easy-clean features enhance maintenance by simplifying the removal of ice, water, and dirt.

Key Features

  • Anti-ice
  • PFA-free
  • Hydrophobic surface
  • Easy-to-clean
  • UV resistance, no discoloration
  • Chemical and thermal resistance
  • Dense and compact coating
  • Good adhesion to various substates

Physical Features

  • Appearance: transparent
  • Color: colorless
  • Solid Content: approx. 40%
  • Curing conditions:
    • At 130°C for 3h
    • At 160°C for 1h

Technical Data

  • Static Ice shear Force Test: 170 kPa
  • Water contact angle: 110-115°
  • Surface Energy (OWRK Method): 15-18 mN/m
  • Water roll-off angle: 16-17°
  • Cured Film Thickness: up to maximum 15 μm (recommended)
  • Adhesion (Cross Hatsch Test ASTM D3359, Method B): ASTM (ISO) Class 5B (0)
  • UV Resistance (ISO 16474-3 C1, 3000h): No visual damage, water contact angle 102°
  • Oxygen/Vapor barrier (boiling water, 24h): No visual damage, water contact angle 106°.

For detailed specifications and application guidelines, please refer to the Technical Data Sheet.

For safety information (SDS), please contact us.

Anti Ice Coating: AAC SLIPS

AAC SLIPS is a hydrophobic, 2K hybrid resin anti-ice coating leveraging SLIPS technology. It creates a slippery, icephobic surface with an ultra-low ice adhesion strength of ~25 kPa, enabling easy ice removal and reducing maintenance. PFAS-free and curing at room temperature, AAC SLIPS offers a safe, simple, and environmentally friendly solution for ice-prone environments.

Key Features

  • Anti-ice
  • PFA-free
  • Hydrophobic
  • Non isocyanate curing (NISO)
  • Room temperature curing
  • Ultra High Solids
  • Good adhesion to various substrates

Physical Features

  • Appearance: opaque
  • Color: black
  • Solid Content: >90 %
  • Curing conditions:
    • Tack-free at room temperature after 8 hours.
    • Fully cured at room temperature after 10 hours.
    • Full chemical / mechanical properties (rt) after 14 days

Technical Data

  • Static Ice shear Force Test: 25 kPa
  • Water contact angle: 102.2-109.5°
  • Surface Energy (OWRK Method): 19.4-23.6 mN/m
  • Water roll-off angle: 18.5-24°
  • Cured Film Thickness: up to maximum 100 μm
  • Adhesion (Cross-cut test, ISO 2409): GT 0
  • Xenon Test (IEC TS 62788-7-2:2017, Condition A3, 1000h):
    • Water contact angle: 108.9°
    • Static Ice shear Force Test: 161 kPa

For detailed specifications and application guidelines, please refer to the Technical Data Sheet.

For safety information (SDS), please contact us.

Anti Ice Coating: AAC White

AAC White is an advanced 2K hybrid system with very good anti-ice properties and minimal ice adhesion. This white-pigmented, room temperature curing solution offers superior protection against corrosion, light, and moisture. Its hydrophobic, low-friction features ensure effective water repellency and reduce ice buildup, making it the ideal choice for durable surface protection in demanding environments.

Key Features

  • Anti-ice
  • Hydrophobic
  • Non isocyanate curing (NISO)
  • High solid
  • Non-stick effect
  • UV resistance
  • Good adhesion to various substrates

Physical Features

  • Appearance: glossy
  • Color: white
  • Solid Content: 72.8 %
  • Mix Ratio (A:B): 1.0 : 0.1
  • Curing conditions:
    • Tack-free at room temperature after 3 hours.
    • Fully cured at room temperature after 24 hours.
    • Full chemical / mechanical properties (rt) after 14 days

Technical Data

  • Static Ice shear force test: 175 kPa
  • Water contact angle: 114-118°
  • Surface Energy (OWRK Method): 11.5 mN/m
  • Water roll-off angle: 25-27°
  • Cured Film Thickness: up to maximum 100 μm
  • Adhesion (Cross-cut test, ISO 2409): GT 0
  • Xenon Test (IEC TS 62788-7-2:2017, Condition A3, 1000h):
    • Slight discoloration
    • Water contact angle: 113°
    • Static ice shear force test: 208 kPa
  • UV Resistance (ISO 16474-3):
    • Water contact angle: 114°
    • Static ice shear force test: 180 kPa

For detailed specifications and application guidelines, please refer to the Technical Data Sheet.

For safety information (SDS), please contact us.

0+
successfully completed ESA projects
0+
years of space experience – since 1989
0+
satisfied international business partners

This is how we approach your project

Our team will analyze your situation and recommend a suitable procedure

Your Content Goes Here

Contact us for a non-binding initial consultation.

Your Content Goes Here

We analyze your requirements and create the right offer for you.

Your Content Goes Here

We involve you interactively in the project implementation until it is successfully completed.